PERMENORM® 5000 H2

  • Ribbons, Sheets, Cuts

    • Thickness 0,35 mm – 3 mm
    • Length < 3000 mm
    • Width < 750 mm
    • Sheets may be purchased complete or cut according to your requirements.
  • Rods, Bars

    • Diameter 5 mm – 215 mm
    • Length as demanded
  • Mögliche weitere Veredelung

    Wir längen ab, besäumen, teilen, biegen, stanzen, schweißen und glühen – von einfachsten Formen bis zu komplizierten Geometrien.


    Mehr erfahren
  • Wärmebehandlung

    Bitte beachten Sie, dass bis auf wenige Ausnahmen nach Abschluss der mechanischen Bearbeitung eine Wärmebehandlung zur Einstellung der weichmagnetischen Eigenschaften zwingend notwendig ist.


    Mehr erfahren

Properties of material

Compared to MUMETALL®, PERMENORM® 5000 H2 with its higher iron content has a higher saturation magnetisation and is therefore suitable primarily for applications in which stronger magnetic fields play a role. PERMENORM® 5000 H2 too does not usually need surface treatment to protect against corrosion.

The higher iron content also has disadvantages, however. Its dynamic properties (at higher magnetic field frequencies) are not as good as with MUMETALL®, and coercive field strength and therefore core losses are greater.

Apart from actuators and yokes, PERMENORM® 5000 H2 is often used in the area of magnetic shielding for medium and higher field strengths.

Typical magnetic properties after annealing
AlloyCompositionµ4 (50 Hz)HC [A/m]BS [T]TCurie [°C]Thermal expansion [10-6/K] (20...100°C)Specific electrical resistance [µOm]Density[g/cm³]
VITROVAC® 6025 X80 % Co2000010,58200121,357,7
VACOPERM® 10080 % NiFe9000020,7840013,50,68,7
MUMETALL®80 % NiFe5000030,8040013,50,68,7
PERMENORM® 5000 H250 % NiFe12000101,55440100,458,25
VACOFLUX® 50 (strip)50 % CoFe1000902,359509,50,358,12
VACOFLUX® 50 (massive)50 % CoFe1000 (static)2002,359509,50,358,12
Soft Iron99,9 % Fe1000 (static)802,15770 0,1077,86
CRYOPERM® 1080 % NiFe**** 0,358,7
TRAFOPERM® N33 % SiFe1000 (static)252,03750120,47,65
µ4: µr at 0,4 A/m